低炭素ステンレス鋼溶接金属の熱時効に関する研究
著者:
三浦 靖史,新井 拓,（電中研）
発刊日:
公開日:
キーワードタグ:
Atom probe tomography Boiling water reactor Fracture toughness Thermal aging Type 316L stainless steels Weld metals
三浦 靖史,新井 拓,（電中研）
発刊日:
公開日:
キーワードタグ:
Atom probe tomography Boiling water reactor Fracture toughness Thermal aging Type 316L stainless steels Weld metals
Fracture toughness tests and atom probe tomography were conducted to evaluate the effect of thermal aging on the fracture toughness and the microstructural evolution in ferrite phase of shielded metal arc weld (SMAW) and gas tungsten arc weld (GTAW) of type 316L stainless steels. The resistance to ductile crack extension of aged welds was lower than that of unaged welds. For the GTAW the effect of aging temperature on the reduction rate of the fracture toughness, which may be due to relatively high ferrite ...
英字タイトル:
Study on Thermal Aging of Stainless Steel Weld Metals
英字タイトル:
Study on Thermal Aging of Stainless Steel Weld Metals
第16回
低炭素ステンレス鋼溶接金属の熱時効特性評価に関する電中研の取組み
著者:
三浦 靖史,赤澤 弾,加古 謙司,新井 拓,（電中研）
発刊日:
公開日:
キーワードタグ:
Boiling water reactor Fracture toughness Stress corrosion cracking Thermal aging Type 316L stainless steel Weld metal
三浦 靖史,赤澤 弾,加古 謙司,新井 拓,（電中研）
発刊日:
公開日:
キーワードタグ:
Boiling water reactor Fracture toughness Stress corrosion cracking Thermal aging Type 316L stainless steel Weld metal
Tensile test, fracture toughness test, and stress corrosion cracking (SCC) test were conducted in order to evaluate the effect of thermal aging on the mechanical properties and SCC crack growth rate of shielded metal arc weld (SMAW) and gas tungsten arc weld (GTAW) of type 316L stainless steel. Thermal aging at 350 oC induced a moderate increase of ultimate tensile strength in both the welds, and the value of GTAW was higher than that of SMAW. The resistance to ductile crack extension of aged welds was lowe...
英字タイトル:
CRIEPI Activities for Evaluation of Thermally Aged Stainless Steel Weld Metals
英字タイトル:
CRIEPI Activities for Evaluation of Thermally Aged Stainless Steel Weld Metals
第15回
強風飛来物衝突確率評価コードTOMAXIの開発とその適用例
著者:
江口 譲,平口 博丸,村上 貴裕,杉本 聡一郎,服部 康男,（電中研）
発刊日:
公開日:
キーワードタグ:
High Wind Missile Strike Probability Tornado Tumbling Typhoon
江口 譲,平口 博丸,村上 貴裕,杉本 聡一郎,服部 康男,（電中研）
発刊日:
公開日:
キーワードタグ:
High Wind Missile Strike Probability Tornado Tumbling Typhoon
Injection of objects into high wind and flight in the air are numerically simulated using a random orientation model in order to mimic the tumbling of the objects. The computed random trajectories are used to evaluate annual strike probability on a target by considering the annual exceedance probability of the wind speed at the points where the objects are initially placed. Assuming that the direction of tornado translational path or the direction of straight wind is stochastically random, such numerical sc...
英字タイトル:
Development of Wind-borne Missile Strike Probability Evaluation Code TOMAXI and Its Application
英字タイトル:
Development of Wind-borne Missile Strike Probability Evaluation Code TOMAXI and Its Application
第16回
我が国における人間信頼性解析の改善状況
著者:
武田 大介,桐本 順広,野々瀬 晃平,弘津 祐子,佐相 邦英,岡本 拓男,（電中研）
発刊日:
公開日:
キーワードタグ:
Extreme Condition Human Error Probability (HEP) Human Failure Event (HFE) Human Reliability Analysis (HRA) Narrative
武田 大介,桐本 順広,野々瀬 晃平,弘津 祐子,佐相 邦英,岡本 拓男,（電中研）
発刊日:
公開日:
キーワードタグ:
Extreme Condition Human Error Probability (HEP) Human Failure Event (HFE) Human Reliability Analysis (HRA) Narrative
In Japan, after the Fukushima Daiichi Nuclear Power Plant accident due to the Great East Japan Earthquake, in addition to risk assessment by traditional conservative approaches, Probabilistic Risk Assessment (PRA) has been used to deal with residual risk caused by extremely rare events. As the evaluation techniques for risk such as external hazards and building/component fragility have been improved, the influence of Human Failure Event (HFE) on overall risk has relatively increased, thus the importance of ...
英字タイトル:
Improvement of Human Reliability Analysis in Japan
英字タイトル:
Improvement of Human Reliability Analysis in Japan
第17回
火力発電プラント配管の破断余寿命診断のデジタルツイン
著者:
高橋 陸,木谷 悠二,小野 進,（大坂府立大）,西田 秀高,（中国電力）,西ノ入 聡,（電中研）,生島 一樹,柴原 正和,（大阪府立大）
発刊日:
公開日:
キーワードタグ:
Creep Digital Twin Life Expectancy Diagnosis Pipe Thermal Power Plant
高橋 陸,木谷 悠二,小野 進,（大坂府立大）,西田 秀高,（中国電力）,西ノ入 聡,（電中研）,生島 一樹,柴原 正和,（大阪府立大）
発刊日:
公開日:
キーワードタグ:
Creep Digital Twin Life Expectancy Diagnosis Pipe Thermal Power Plant
In recent years, there has been a growing demand for power generation from renewable energy sources. However, power generation from renewable energy sources is characterized by the fact that it is highly dependent on weather conditions, and thermal power generation requires large changes in output to adjust power. The sudden changes in temperature and strain that occur during this process have a significant impact on the remaining life of the equipment. In this study, we developed a system to identify inter...
英字タイトル:
Digital Twin for Fracture Life Expectancy Diagnosis of Thermal Power Plant Pipe
英字タイトル:
Digital Twin for Fracture Life Expectancy Diagnosis of Thermal Power Plant Pipe
原子力事業者は、福島第一原子力発電所事故後にリスク情報を活用した意思決定（RIDM）プロセス を、発電所のマネジメントに導入することとし、そのための取り組み方針等を 2018 年 2 月「リスク情報活用の実現に向けた戦略プラン及びアクションプラン」に取りまとめ、2020 年 6 月にその後の取り組み状況を踏まえ、同プランを改訂した。同プランの概要及び NRRC における同プランをサポートするための取り組みを概説する。...
英字タイトル:
Current efforts to utilize RIDM process
英字タイトル:
Current efforts to utilize RIDM process
原子力事業者は自律的な安全性向上に向けてリスク情報を活用した意思決定を導入し、パフォーマンスベース・リスクインフォームドの自律的なマネジメントに変革することを宣言した。原子力リスク研究センター(NRRC)は、事業者のリスク情報活用の実現に向けた取り組みに対し、PRA を中心として様々な形で、電気事業連丘会、原子力安全推進協会(JANSI)と連携しながら支援しており、今後も継続していく。...
電力中央研究所原子力リスク研究センター(NRRC)は、トレーサビリプイの確保された確率論的リスク評価(PRA)用データを収集するための「確率論的リスク評価(PRA)のためのデータ収集実施ガイド」を電力事業者と協力して策定した。これらのデータ収集の取り組みについて紹介する。...
英字タイトル:
Development of a database used in probabilistic risk assessment
英字タイトル:
Development of a database used in probabilistic risk assessment
第17回
確率論的リスク評価用原子力機器信頼性パラメータの整備
著者:
吉田 智朗,清野 弘章,喜多 利亘,古田 泰,（電中研）
発刊日:
公開日:
キーワードタグ:
Bayesian Component failure probability Component failure rate Component reliability parameter Probabilistic risk assessment
吉田 智朗,清野 弘章,喜多 利亘,古田 泰,（電中研）
発刊日:
公開日:
キーワードタグ:
Bayesian Component failure probability Component failure rate Component reliability parameter Probabilistic risk assessment
New reliability parameters of the nuclear components have been estimated for probabilistic risk assessment in Japan. The data for the estimation were collected in a manner consistent with their PRA modeling under the utilities quality assurance systems. The component reliability parameters were estimated with empirical Bayes method. These reliability parameters will contribute to the improvement of the PRA quality in Japan....
英字タイトル:
Development of Nuclear Component Reliability Parameters for Probabilistic Risk Assessment in Japan
英字タイトル:
Development of Nuclear Component Reliability Parameters for Probabilistic Risk Assessment in Japan
第16回
竜巻飛来物の建屋等への年間衝突確率評価法の開発
著者:
江口 譲,平口 博丸,村上 貴裕,杉本 聡一郎,服部 康男,（電中研）
発刊日:
公開日:
キーワードタグ:
Building Missile Strike Probability Structure Tornado
江口 譲,平口 博丸,村上 貴裕,杉本 聡一郎,服部 康男,（電中研）
発刊日:
公開日:
キーワードタグ:
Building Missile Strike Probability Structure Tornado
A computer code, TOMAXI, was developed to evaluate annual strike probability of a tornado-borne missile for a vertical or horizontal plate of unit area placed in an arbitrary position in our previous study, assuming that the direction of tornado translational path is stochastically random. In the present study, the authors have extended the function of TOMAXI to compute annual strike probability of a tornado-borne missile for a building or a structure of arbitrary shape placed in an arbitrary position. As a...
英字タイトル:
Development of Evaluation Method for Annual Strike Probability of Tornado-borne Missile on Buildings and Structures
英字タイトル:
Development of Evaluation Method for Annual Strike Probability of Tornado-borne Missile on Buildings and Structures