Austenitic stainless steel (SUS316L) was used as specimen material, and the plate specimens were deformed plastically with a wide range of strain rates (6.67×10-5~ 6.70×102 /s). The residual micro-stress for each lattice plane was measured with hard synchrotron X-rays. The residual macro-stress due to tensile deformation de- pended on strain rate. The residual micro-stresses varied from tension to compression, depending on the dif- fraction elastic constant. The soft lattice plane had tensile residual stress, and the hard lattice plane had com- pressive residual stress. The higher the strain rate, the smaller the difference in residual micro-stresses. The re- sidual micro-stresses of the surfaces peened with the laser-peening or water-jet-peening were examined. Both surfaces had exhibited large compressive residual stress. The residual micro-stress on the peened surfaces showed a tendency opposite to residual micro-stress due to tensile deformation.

---