BWR炉内構造物のニッケル基合金溶接部に発見された応力腐食割れの超音波探傷試験結果とその評価


英字タイトル:
Evaluation on Ultrasonic Examination Methods applied to Ni-base Alloy Weld including Cracks due to Stress Corrosion Cracking found in BWR Reactor Internal
著者:
青木 孝行 Takayuki AOKI 樋口 真一 Shinichi HIGUCHI 小林 広幸 Hiroyuki KOBAYASHI 清水 禎人 Sadato SHIMIZU
発刊日:
公開日:
カテゴリ: 論文
キーワードタグ:

概要

A Ni-base alloy weld, including cracks due to stress corrosion cracking found in the reactor internal of the oldest BWR in Japan, Tsuruga unit 1, in 1999, was examined by three (3) types of UT method. After this examination, a depth of each crack was confirmed by carrying out a little excavation with a grinder and PT examination by turns until each crack disappeared. Then, the depth measured by the former method was compared with the one measured by the latter method. In this fashion, performances of the UT methods were verified. As a result, a combi- nation of the three types of UT method was found to meet the acceptance criteria given by ASME Sec.XI Appendix VIII, Performance Demonstration for Ultrasonic Examination Systems-Supplement 6. In this paper, the results of the UT examination described above and their evaluation are discussed.


全文掲載のPDFファイルダウンロード