東海再処理施設における海中放出管からの漏えいについて -海中放出管の漏えい原因究明(その3)再発防止対策及び管理方法-
英字タイトル:
Liquid leakage from the sea release pipe of the Tokai reprocessing plant estigation into the cause of the leak (3): Preventive measures against recurrences and the management metho - Investigation into the cause of the leak (3): Preventive measures against recurrences and the management method
著者:
西田 恭輔 Kyosuke NISHIDA 鋤柄 光二 Kouji SUKIGARA 照沼 朋広 Tomohiro TERUNUMA 岩﨑 省悟 Shogo IWASAKI 伊波 慎一 Shinichi INAMI
発刊日:
公開日:
cathodic protection systemsea release pipe
Liquid leakage from the sea release pipe of the Tokai reprocessing plant estigation into the cause of the leak (3): Preventive measures against recurrences and the management metho - Investigation into the cause of the leak (3): Preventive measures against recurrences and the management method
著者:
西田 恭輔 Kyosuke NISHIDA 鋤柄 光二 Kouji SUKIGARA 照沼 朋広 Tomohiro TERUNUMA 岩﨑 省悟 Shogo IWASAKI 伊波 慎一 Shinichi INAMI
発刊日:
公開日:
カテゴリ: 第8回
キーワードタグ:cathodic protection systemsea release pipe
概要
1. 緒言平成21年4月に確認された東海再処理施設の海中放 出設備の漏えい事象は、漏えい箇所が海底埋設の放出 管であった。漏えいの原因は、放出管の施工時に損傷 し、経年変化として損傷箇所に電気防食で発生した水 素が影響したことで水素脆性割れが起こり、き裂が発 生、さらには水素誘起割れによりき裂が進展し貫通し たことによるものと推定した。損傷箇所に水素脆性割れが生じる原因となった水素 は電気防食によるものであり、このときの防食電位と 水素発生の関係等の調査を行った。この結果、損傷が 素が影響したことで水素脆...